0.005X100mm Thickness Evanohm Foil for Rjk Type High Precision Alloy Foil Resistor

• Application: Aviation, Electronics
• Standard: GB, DIN, ASTM, AISI
• Purity: 80%
• Alloy: Alloy
• Type: Foil
• Powder: Not Powder
• Model NO.: Evanohm
• Chemical Composition: Ni 80%
• Product Name: Evanohm Foil
• Characteristics: High Resistivity, Good Oxidation Resistance
• The Highest Use Temperature: 400c
• Density: 8.1g/cm3
• Resisivity: 1.33
• Thickness: 5 Um
• Width: 100mm
• MOQ: 1kg
• Color: Silver White
• Usage: Film Resistor
• Transport Package: Wooden Cases or Cartons
• Specification: 0.005mm
• Trademark: HUONA
• Origin: Shanghai
• HS Code: 7505220000
• Production Capacity: 50 Ton/Month

Product Description

0.005x100mm thickness Evanohm foil for RJK type high precision alloy foil resistor

1.   Evanohm alloy

Evanohm alloy is made up of copper, nickel, Aluminum and chromium as the main components. The resistivity is 2~3 times higher thanmanganin. 
It has lower temperature coefficient of resistance(TCR), lower thermal EMF versus copper, good permanence of resistance for a long period of time 
and strong antioxidation. Its working temperature range is wider than manganin (-60~300ºC). 
It is suitable for making fine precision resistance elements and strain.

 2.  Evanohm size

Wire: 0.01mm-10mm
Ribbon: 0.05*0.2mm-2.0*6.0mm
Strip: 0.5*5.0mm-5.0*250mm
 

3.Karma  Property

name	code	Main Composition (%)				Standard
		Cr	Al	Cu	Ni
Evanohm	6J23	19~21	2.7~3.2	2.0~3.0	bal.	JB/T 5328

 

Name	Code	(20ºC)  Resisti   vity (μΩ.m)	(20ºC)  Temp. Coeff.  Of Resistance  (αX10-6/ºC)	(0~100ºC)  Thermal   EMF vs.   Copper  (μv/ºC)	Max.workin        g Temp.(ºC)	(%) Elongati     on	(N/mm2)  Tensile  Strength	Standard
Evanohm	6J23	1.33±0.07	≤±20	≤2.5	≤300	>7	≥780	JB/T 5328

4. Distinctive features of Evanohm resistance wire

1) Starting with Nickel Chromium electric heat wire Class 1, we replaced some of the Ni with
Al and other elements, and thus achieved a precision resistance material with improved
resistance temperature coefficient and heat electromotive force against copper.
With the addition of Al, we have succeeded in making volume resistivity 1.2 times greater
than Nickel Chromium electric heat wire Class 1 and the tensile strength 1.3 times greater.

2) The secondary temperature coefficient β of Evanohm alloy wire KMW is very small, - 0.03 × 10-6/ K2,

and the resistance temperature curve turns out to be almost a straight line within a wide
temperature range.

Therefore, the temperature coefficient is set to be the average temperature coefficient between
23 ~ 53 °C, but 1 × 10-6/K, the average temperature coefficient between 0 ~ 100 °C, also may
be adopted for the temperature coefficient.

3) Electromotive force against copper between 1 ~ 100 °C is also small, below + 2 μV/K, and

exhibits excellent stability over a period of many years.

4) If this is to be used as a precision resistance material, low temperature heat treatment is
required to eliminate processing distortions just as in the case of Manganin wire CMW.