Audited Supplier | Ni | 78.5~80.0 | Fe | Bal. | Mn | 0.6~1.1 | Si | 0.3~0.5 |
| Mo | 3.8~4.1 | Cu | ≤0.2 | ||||
| C | ≤0.03 | P | ≤0.02 | S | ≤0.02 |
| Yield strength | Tensile Strength | Elongation |
| Mpa | Mpa | % |
| 980 | 1030 | 3~50 |
| Density (g/cm3) | 8.6 |
| Electrical resistivity at 20ºC(Om*mm2/m) | 0.55 |
| Coefficient of linear expansion(20ºC~200ºC)X10-6/ºC | 10.3~11.5 |
| Saturation magnetostriction coefficient λθ/ 10-6 | 2.0 |
| Curie point Tc/ ºC | 450 |
| The magnetic properties of alloys with high permeability in weak fields |
|||||||
| 1J79 | Initial permeability | Maximum permeability | Coercivity | Saturation magnetic induction intensity | |||
| Сold-rolled strip/ sheet. Thickness, mm |
μ0.08/ (mH/m) | μm/ (mH/m) | Hc/ (A/m) | BS/ T | |||
| ≥ | ≤ | ||||||
| 0.01 mm | 17.5 | 87.5 | 5.6 | 0.75 |
|||
| 0.1~0.19 mm | 25.0 | 162.5 | 2.4 | ||||
| 0.2~0.34 mm | 28.0 | 225.0 | 1.6 | ||||
| 0.35~1.0 mm | 30.0 | 250.0 | 1.6 | ||||
| 1.1~2.5 mm | 27.5 | 225.0 | 1.6 | ||||
| 2.6~3.0 mm | 26.3 | 187.5 | 2.0 | ||||
| cold drawn wire | |||||||
| 0.1 mm | 6.3 | 50 | 6.4 | ||||
| Bar | |||||||
| 8-100 mm | 25 | 100 | 3.2 | ||||
| Mode of heat treatment 1J79 | |
| Annealing media | Vacuum with a residual pressure not higher than 0.1Pa, hydrogen with a dew point of not higher than minus 40 ºC. |
| The heating temperature and rate | 1100~1150ºC |
| Holding time | 3~6 |
| Cooling rate | With 100 ~ 200 ºC/ h cooled to 600 ºC, rapidly cooled to 300º |
| Alloys Name | Type | Dimension | ||
| OhmAlloy-1J79 | Wire | D= 0.1~8mm | ||
| OhmAlloy-1J79 | Strip | W= 8~390mm | T= 0.3mm | |
| OhmAlloy-1J79 | Foil | W= 10~100mm | T= 0.01~0.1 | |
| OhmAlloy-1J79 | Bar | Dia= 8~100mm | L= 50~1000 | |