Permalloy Precision Alloy Ni46 Strip for Low-Loss Micro-Motor

• Customization: Available
• Classification: 1j46
• Product Type: Strip
• Model NO.: Ni46 Strip
• Material: Feni Alloy
• Model No.: Alloy1j46
• Sample: Free Sample
• Density, g/cm3: 8.2
• Application: Magnetic Field
• Curie Point Tc/ ºC: 400
• Certificate: SGS, ISO, RoHS
• Resistivity(μΩ.M): 0.45
• Surface Treatment: Bright or Oxidation
• Saturation Magnetostriction Coefficient: 25
• Transport Package: Coil+ Waterproof Paper+ Wooden Case
• Specification: Base on customers′ request
• Trademark: HUONA
• Origin: Shanghai
• HS Code: 7204290000
• Production Capacity: 20000 Tons/Year

Product Description

1J46  (Soft magnetic alloy)
(Common Name: Ni46, E11e, 46H, 45-permalloy, PB)
 
1J46 is a nickel-iron magnetic alloy, with about 46% nickel and iron content. It is derived in accordance with permalloy. It has characteristics of high permeability and high saturation magnetic flux density.
Alloy melting in a vacuum medium, cast into ingots, after hot forging blanks made of sheet metal, and then after hot rolling, pickling, surface treatment, cold rolling into finished products.
1J46 Iron-nickel alloy( soft magnetic alloy) mostly in an alternating magnetic field used mainly for high magnetic yoke, sensitive relays, low-loss micro-motor, small power transformers, pulse transformer, transistor switches, magnetic amplifier magnetic modulator, sensitive signal input and output transformers, magnetic heading aviation instrumentation magnetic sensor, magnetic susceptibility measurement instrument components, precision meter movable piece and the stator magnetic shielding and magnetic temperature compensation element.
 
Normal composition%

Ni	45~46.5	Fe	Bal.	Mn	0.6~1.0	Si	0.15~0.3
Mo	-	Cu	≤0.2
C	≤0.03	P	≤0.02	S	≤0.02

 
Typical Mechanical properties

Yield strength	Tensile Strength	Elongation
Mpa	Mpa	%
-	-	3~35

 
Typical Physical properties

Density (g/cm3)	8.2
Electrical resistivity at 20ºC(Om*mm2/m)	0.45
Coefficient of linear expansion(20ºC~200ºC)X10-6/ºC	-
Saturation magnetostriction coefficient λθ/ 10-6	25,0
Curie point   Tc/ ºC	400

 

The magnetic properties of alloys with high permeability in weak fields
1J46	Initial permeability	Maximum permeability			Coercivity	Saturation magnetic induction intensity
Сold-rolled strip/ sheet. Thickness, mm	μ0.08/ (mH/m)		μm/ (mH/m)	Hc/ (A/m)			BS/ T
	≥			≤
0.02~0.04 mm	1.6		22.5	32.0			1.5
0.1~0.19 mm	2.5		31.3	20.0
0.2~0.34 mm	3.1		37.5	16.0
0.35~2.50 mm	3.5		45.0	12.0
Bar
8-100 mm	2.5		31.3	16.0

 

Mode of heat treatment
Annealing media	Vacuum with a residual pressure not higher than 0.1Pa, hydrogen with a dew point of not higher than minus 40 ºC.
The heating temperature and rate	1100~1150ºC
Holding time/h	3~6
Cooling rate	With 100 ~ 200 ºC/ h cooled to 600 ºC, Rapid cooling to 300 baked