HUONA NiAl 95/5 wire is a solid wire specifically designed for arc spray systems. It is self-bonding to most materials and requires minimal surface preparation.
Bond strengths in excess of 9000 psi can be achieved on clean smooth surfaces. Roughening of the surface by machining, grit blasting or grinding can increase the bond strength up to 10,000 psi.
NiAl 95/5 wire exhibits good resistance to high temperature oxidation and abrasion, and excellent resistance to impact and bending.
NiAl 95/5 wire can be machined and ground to a finish of 5 micro inches. It is a self-bonding, one step material and is also suitable for the build-up and dimensional restoration of nickel-based alloys.
NiAl 95/5 wire is widely used as a bond coat for subsequent thermal spray topcoats and as a one step build up material for dimensional restoration of aircraft engines.
NiAl 95/5 Wires are packed in DIN300 spool.
Mechanical Properties
Products: NiAl 95/5 Wire
| Typical Hardness |
HRB 75 |
| Bond Strength |
10,000 psi |
| Deposit Rate |
10 lbs/hr/100A |
| Deposit Efficiency |
70% |
| Surface Texture |
Variable |
| Machineability |
Good |
Surface Preparation
Surface shuold be clean, white metal, with no oxides(rust), dirt, grease, or oil on the surface to be coated. Note: It is best not to handle surfaces after cleaning.
Recommended method of preparation is to grit blast with 24 mesh aluminum oxide, rough grind, or rough machine in a lathe.
Size & Packaging
| Condition |
Solid wire |
| Diameter |
1.6mm(14 ga), 2.0mm, 3.175mm |
| Package Size |
10kg, 15kg, or up to client's demand |
The Wires will be packed in the box and then put in the wooden box or on the wooden pallet
Transportation
ByExpress(DHL, FedEx, TNT, UPS), By sea, By air, By train
Audited Supplier 
){kind=link}