Permalloy 1j85/1j86/1j79 Soft Magnetic Alloy Wire

• Application: Aviation, Electronics, Industrial, Medical, Chemical
• Standard: GB, DIN, ASTM
• Purity: 80%
• Alloy: Alloy
• Type: Nickel Wire
• Powder: Not Powder
• Model NO.: 1j86
• Resisivity: 0.56
• Density: 8.75 Cm3
• Curie Point: 400 C
• Name: Ni80mo4
• Hardness: 130~240 Hv
• Tensile Strength: 560~930 MPa
• Yield Strength: 150~885 MPa
• Elongation: 4~40 %
• Use: High Frequency Inductive Components
• Transport Package: Wooden Case
• Specification: 0.7mm
• Trademark: HUONA
• Origin: Shanghai
• HS Code: 75062000
• Production Capacity: 200ton/Month

Product Description

Permalloy 1j85/1j86/1j79 Soft Magnetic Alloy Wire

Soft magnetic alloy are in weak magnetic field with high permeability and low coercive force of alloys.This kind of alloy are widely used in radio electronics, precision instruments and meters, remote control and automatic control system, the combination is mainly used for energy conversion and information processing, the two aspects of is an important material in the national economy.
Introduction to the

Chemical composition

composition	C	P	S	Mn	Si
	≤
Content(%)	0.03	0.02	0.02	0.3~0.6	0.15~0.3

 

composition	Ni	Cr	Mo	Cu	Fe
Content(%)	79.0~81.0	-	4.8~5.2	≤0.2	Bal

Heat treatment system

shop sign	Annealing medium	heating temperature	Keep the temperature time/h	Cooling rate
1j85	Dry hydrogen or vacuum, pressure is not greater than 0.1 Pa	Along with the furnace heating up 1100~1150ºC	3~6	In 100 ~ 200 ºC / h speed cooling to 600 ºC, fast to 300 ºC draw a charge

Soft magnetic alloy outer magnetic field under the action of easy magnetization, basic disappear after removal of magnetic field of magnetic induction intensity and magnetic alloys.

2.Usage 
It is mostly used in small transformers, pulse transformers, relays, transformer, magnetic amplifier, electromagnetic clutch,the reactor coreand magnetic shielding which work inweak magnetic orsecondary magnetic field.
 
3.Features 
1).Low coercivity and magnetic hysteresis loss;
2).High resistivity and loweddy-currentloss;
3).High initialmagnetic permeability and maximum magnetic permeability;
4).High saturation magnetic flux density;
 
4. Packing detail
 
 1). Coil (plastic spool) + compressed ply-wooden case + pallet 
 2). Coil (plastic spool) + carton + pallet