0.2mm 130 Class Enamelled Leader Colored Round Copper Alloy Wire

• Customization: Available
• Insulation Level: H, F, B, E
• Certification: ISO9001, RoHS
• Model NO.: Enamelled Wire
• Brand: Huona
• Application: Transformer, Instrument, Electrical Equipment, Motor
• Shape: Round Wire
• Conductor Material: Copper Wire
• Serves: Small Order Accepted
• Size: Sample Available
• Other Name: Eureka Wire
• OEM: Yes
• Stock: Seyn
• Sample (Less Than1kg): Can Discuss
• Material: Cunimn Alloy
• Transport Package: Woodren Case or Cartons
• Specification: 0.01-3mm
• Trademark: HUONA
• Origin: Shanghai
• HS Code: 7408229000
• Production Capacity: 2000tons/Year

Product Description

0.1mm 80 Degrees Red/Bule Color polyuerthane Enamelled Copper Wire

Product Description

Magnet wire or enameled wire is a copper or aluminum wire coated with a very thin layer of insulation. It is used in the construction of transformers, inductors, motors, generators, speakers, hard disk head actuators, electromagnets, electric guitar pickups and other applications that require tight coils of insulated wire.

The wire itself is most often fully annealed, electrolytically refined copper. Aluminum magnet wire is sometimes used for large transformers and motors. The insulation is typically made of tough polymer film materials rather than enamel, as the name might suggest.

Conductor
The most suitable materials for magnet wire applications are unalloyed pure metals, particularly copper. When factors such as chemical, physical, and mechanical property requirements are considered, copper is considered the first choice conductor for magnet wire.

Most often, magnet wire is composed of fully annealed, electrolytically refined copper to allow closer winding when making electromagnetic coils. High-purity oxygen-free copper grades are used for high-temperature applications in reducing atmospheres or in motors or generators cooled by hydrogen gas.

Aluminium magnet wire is sometimes used as an alternative for large transformers and motors. Because of its lower electrical conductivity, aluminium wire requires a 1.6-times larger cross sectional area than a copper wire to achieve comparable DC resistance.

Tpye of Insulation:

Enameled Type	Polyester	Modified Polyester	polyester-imide	Polyamide-imide	polyester-imide /Polyamide-imide
Insulation Type	PEW/130	PEW(G)/155	EIW/180	EI/AIW/200	EIW(EI/AIW)220
Thermal class	130, CLASS B	155, CLASS F	180, CLASS H	200, CLASS C	220, CLASS N
Standard	IEC60317-0-2 IEC60317-29 MW36-A	IEC60317-0-2 IEC60317-29MW36-A	IEC60317-0-2 IEC60317-29 MW36-A	IEC60317-0-2 IEC60317-29 MW36-A	IEC60317-0-2 IEC60317-29 MW36-A

 

		Constantan 6J40	New Constantan	Manganin	Manganin	Manganin
			6J11	6J12	6J8	6J13
Main Chemical Elements %	Mn	1~2	10.5~12.5	11~13	8~10	11~13
	Ni	39~41	-	2~3	-	2~5
	Cu	REST	REST	REST	REST	REST
			Al2.5~4.5 Fe1.0~1.6		Si1~2
Temperature Range for Components		5~500	5~500	5~45	10~80	10~80
Density		8.88	8	8.44	8.7	8.4
g/cm3
Resistivity		0.48	0.49	0.47	0.35	0.44
μΩ.m,20		±0.03	±0.03	±0.03	±0.05	±0.04
Extensibility		≥15	≥15	≥15	≥15	≥15
%Φ0.5
Resistance		-40~+40	-80~+80	-3~+20	-5~+10	0~+40
Temperature
Quotiety
α,10 -6 /
Thermoelectromotive		45	2	1	2	2
force to Copper
μv/(0~100)

Tpye of Bare Wire

main property type		Cuni1	CuNI2	CuNI6	CuNI10	CuNi19	CuNi23	CuNi30	CuNi34	CuNI44
main chemical composition	Ni	1	2	6	10	19	23	30	34	44
	MN	/	/	/	/	0.5	0.5	1.0	1.0	1.0
	CU	rest	rest	rest	rest	rest	rest	rest	rest	rest
max  working temperature		/	200	220	250	300	300	350	350	400
density  g/cm3		8.9	8.9	8.9	8.9	8.9	8.9	8.9	8.9	8.9
resistivity  at 20 °c		0.03  ± 10%	0.05 ±10%	0.1 ±10%	0.15 ±10%	0.25 ±5%	0.3 ±5%	0.35 ±5%	0.40 ±5%	0.49 ±5%
temperature coefficient of resistance		<100	<120	<60	<50	<25	<16	<10	-0	<-6
tensile strength mpa		>210	>220	>250	>290	>340	>350	>400	>400	>420
elongation		>25	>25	>25	>25	>25	>25	>25	>25	>25
melting point °c		1085	1090	1095	1100	1135	1150	1170	1180	1280
coefficient of conductivity		145	130	92	59	38	33	27	25	23