Evanohm/6j22 Resistance Nichrome Strip for Heating Cable

• Application: Aviation, Electronics, Industrial, Medical, Chemical
• Standard: JIS, GB, DIN, ASTM, AISI
• Purity: 80%Ni
• Alloy: Alloy
• Type: Nickel Strip
• Powder: Not Powder
• Model NO.: Evanohm
• Density: 8.1g/cm3
• The Highest Use Temperature: 1300c
• Resisivity: 1.33
• Characteristics: High Resistivity, Good Oxidation Resistance
• Surface: Bright
• Sample: Free
• Shape: Strip/Wire/Ribbon/Pipe/Sheet/Bar/Foil
• OEM: Yes
• Transport Package: Wooden Cases or Cartons
• Specification: 0.01-8.0mm
• Trademark: Huona
• Origin: China
• HS Code: 7506200000
• Production Capacity: 2000ton/Year

Product Description

Evanohm/6J22 Resistance Nichrome Strip for Heating cable

1.   Evanohm alloy

Evanohm alloy is made up of copper, nickel, Aluminum and Iron as the main components. The resistivity is 2~3 times higher than MENTONG. It has lower temperature coefficient of resistance(TCR), lower thermal EMF versus copper, good permanence of resistance for a long period of time and strong anti-oxidation. Its working temperature range is wider than MENTONG (-60~300ºC). It is suitable for making fine precision resistance elements and strain.

 2.  Evanohm size

Wire: 0.018mm-10mm
Ribbon: 0.05*0.2mm-2.0*6.0mm
Strip: 0.5*5.0mm-5.0*250mm
Bar: 10-100mm

3.Evanohm  Property

name	code	Main Composition (%)				Standard
		Cr	Al	Fe	Ni
Evanohm	6J22	19~21	2.5~3.2	2.0~3.0	bal.	JB/T 5328

 

Name	Code	(20ºC)  Resisti   vity (μΩ.m)	(20ºC)  Temp. Coeff.  Of Resistance  (αX10-6/ºC)	(0~100ºC)  Thermal   EMF vs.   Copper  (μv/ºC)	Max.workin        g Temp.(ºC)	(%) Elongati     on	(N/mm2)  Tensile  Strength	Standard
Evanohm	6J22	1.33±0.07	≤±20	≤2.5	≤300	>7	≥780	JB/T 5328

4. Distinctive features of Evanohm resistance wire

1) Starting with Nickel Chromium electric heat wire Class 1, we replaced some of the Ni with
Al and other elements, and thus achieved a precision resistance material with improved
resistance temperature coefficient and heat electromotive force against copper.
With the addition of Al, we have succeeded in making volume resistivity 1.2 times greater
than Nickel Chromium electric heat wire Class 1 and the tensile strength 1.3 times greater.

2) The secondary temperature coefficient β of Karmalloy wire KMW is very small, - 0.03 × 10-6/ K2,

and the resistance temperature curve turns out to be almost a straight line within a wide
temperature range.

Therefore, the temperature coefficient is set to be the average temperature coefficient between
23 ~ 53 °C, but 1 × 10-6/K, the average temperature coefficient between 0 ~ 100 °C, also may
be adopted for the temperature coefficient.

3) Electromotive force against copper between 1 ~ 100 °C is also small, below + 2 μV/K, and

exhibits excellent stability over a period of many years.

4) If this is to be used as a precision resistance material, low temperature heat treatment is
required to eliminate processing distortions just as in the case of Manganin wire CMW.