Alloy 52 - Fe-Ni Sealing Alloy Tube
Introducing NIFE 52 / FENI52 / Nilo 52 / UNS / UNS N14052 Fe-Ni sealing alloy tube from Huona (Shanghai) New Material Co., Ltd. This alloy contains 52% nickel and 48% iron, making it ideal for use in the telecommunications industry and various electronic applications, especially for glass seals.
Alloy 52 is specifically designed for glass-to-metal sealing applications, offering a nearly constant coefficient of thermal expansion up to 1050F (565 C).
Size Range:
- Sheet: Thickness: 0.1mm~40.0mm, Width: ≤300mm, Condition: Cold rolled (hot), bright, bright annealed
- Round Wire: Diameter: 0.1mm~5.0mm, Condition: Cold drawn, bright, bright annealed
- Flat Wire: Diameter: 0.5mm~5.0mm, Length: ≤1000mm, Condition: Flat rolled, bright annealed
- Bar:
- Diameter: 5.0mm~8.0mm, Length: ≤2000mm, Condition: Cold drawn, bright, bright annealed
- Diameter: 8.0mm~32.0mm, Length: ≤2500mm, Condition: Hot rolled, bright, bright annealed
- Diameter: 32.0mm~180.0mm, Length: ≤1300mm, Condition: Hot forging, peeled, turned, hot treated
- Capillary: Outer Diameter: 8.0mm~1.0mm, Inner Diameter: 0.1mm~8.0mm, Length: ≤2500mm, Condition: Cold drawn, bright, bright annealed
- Pipe: Outer Diameter: 120mm~8.0mm, Inner Diameter: 8.0mm~129mm, Length: ≤4000mm, Condition: Cold drawn, bright, bright annealed
Chemistry:
| |
Cr |
Al |
C |
Fe |
Mn |
Si |
P |
S |
Ni |
Mg |
| Min |
-- |
-- |
-- |
-- |
-- |
-- |
-- |
-- |
50.5 |
-- |
| Max |
0.25 |
0.10 |
0.05 |
Bal. |
0.60 |
0.30 |
0.025 |
0.025 |
-- |
0.5 |
Average Linear Expansion Coefficient:
| Grade |
α1/10-6ºC-1 |
| 20~100ºC |
20~200ºC |
20~300ºC |
20~350ºC |
20~400ºC |
20~450ºC |
20~500ºC |
20~600ºC |
| 4J52 |
10.3 |
10.4 |
10.2 |
10.3 |
10.3 |
10.3 |
10.3 |
10.8 |
Properties:
| Condition |
Approx. tensile strength |
Approx. operating temperature |
| N/mm² |
ksi |
°C |
°F |
| Annealed |
450 - 550 |
65 - 80 |
up to +450 |
up to +840 |
| Hard Drawn |
700 - 900 |
102 - 131 |
up to +450 |
up to +840 |
| Forming: |
| The alloy has good ductility and can be formed by standard means. |
| Welding: |
| Welding by conventional methods is appropriate for this alloy. |
| Heat Treatment: |
| Alloy 52 should be annealed at 1500F followed by air cooling. Intermediate strain relieving can be performed at 1000F. |
| Forging: |
| Forging should be done at a temperature of 2150 F. |
| Cold Working: |
| The alloy is readily cold worked. Deep drawing grade should be specified for that forming operation and annealed grade for general forming. |