MIG TIG Nickel Alloy Welding Wire Erni-1

• Customization: Available
• Application: Electronics, Industrial, Medical
• Standard: JIS, GB, DIN, BS, ASTM, AISI
• Model NO.: ERNi-1
• Purity: -
• Alloy: Alloy
• Type: Nickel Wire
• Powder: Not Powder
• Sample: Free
• Welding Power: DC
• Delivery Time: 5-15days of Erni-1
• Name: Erni-1
• Surface: Bright
• Criterion: ASTM Aws
• Diameter: 1.6mm
• Transport Package: Spool+Case
• Specification: 0.9-4.0
• Trademark: HUONA
• Origin: Shanghai, China
• HS Code: 7505220000
• Production Capacity: 2000 Tons/Year

Product Description

TIG Erni-1 Asme Sfa 5.14 Welding Rod

INTRODUCTION
1 is used for the welding of Nickel 200 and 201. The reaction of titanium with carbon maintains a low level of free carbon and enables the filler metal to be used with Nickel 201. The weld metal of ERNi-1 has good corrosion resistance, particularly in alkalis. 
 
Common Names: Oxford Alloy® 61 FM61
Standard: ASME SFA 5.14   UNS N02061    AWS 5.14     AWS ERNi-1
 
CHEMICAL COMPOSITION(%)

C	Si	Mn	S	P	Ni
≤0.05	0.35-0.5	≤0.9	≤0.01	≤0.01	≥95.0
Al	Ti	Fe	Cu	others
≤1.5	2.0-3.5	≤1.0	≤0.15	<0.5

 
WELDING PARAMATERS

Process	Diameter	Voltage	Amperage	Gas
TIG	.035"     (0.9mm) .045"     (1.2mm)   1/16"     (1.6mm)  3/32"     (2.4mm)   1/8"      (3.2mm)	12-15 13-16 14-18 15-20 15-20	60-90           80-110 90-130 120-175 150-220	100% Argon 100% Argon  100% Argon 100% Argon 100% Argon
MIG	.035"     (0.9mm) .045"     (1.2mm)   1/16"     (1.6mm)	26-29 28-32 29-33	150-190 180-220 200-250	75% Argon + 25% Helium 75% Argon + 25% Helium 75% Argon + 25% Helium
SAW	3/32"     (2.4mm)   1/8"      (3.2mm)     5/32"     (4.0mm)	28-30 29-32 30-33	275-350             350-450   400-550	Suitable Flux may be used Suitable Flux may be used Suitable Flux may be used

 
MECHANICAL PROPERTIES

Tensile Strength	66,500 PSI	460 MPA
Yield Strength	38,000 PSI	260 MPA
Elongation	28%

 
APPLICATIONS
1 nickel based welding wire is used for joining nickel 200 and nickel 201. This includes ASTM grades such as B160 - B163, B725 and B730. 
· Used in a variety of dissimilar applications between nickel alloys to stainless or ferritic steels. 
· Used for overlaying carbon steel and in repairing cast iron castings.