High atmosphere temperature APM Resistance Wire used for Furnace elements
This product takes refined master alloy as raw material, uses powder metallurgy technology to manufacture alloy ingots, and is manufactured by special cold and hot processing and heat treatment process. The product has the advantages of strong oxidation resistance, good corrosion resistance at high temperature, small creep of electrothermal components, long service life at high temperature and small change of resistance. It is suitable for high temperature 1420 C, high power density, corrosive atmosphere, carbon atmosphere and other working environments. It can be used in ceramic kilns, high temperature heat treatment furnaces, laboratory furnaces, electronic industrial furnaces and diffusion furnaces.
Advantages
High atmosphere temperature Long life
High surface load Good oxidation resistance
Small proportion High resistivity
Good sulfur resistance
Specifications
Wire diameter range : φ0.1-8.5 mm
Flat Wire Thickness : 0.1-0.4 mm Width:0.5-4.5 mm
Flat Strip Thickness : 0.5-2.5 mm Width:5.0-48 mm
Main composition(Wt%)
| |
C |
Si |
Mn |
Cr |
Al |
Fe |
| Min |
- |
- |
- |
20 |
5.5 |
Bal. |
| Max |
0.04 |
0.5 |
0.4 |
22 |
6.0 |
Bal. |
Main mechanical properties
| Tensile Strength at Room Tmperature |
Elongation |
Hardness |
Tensile Strength at 1000ºC |
High Temperature Durability At 1000ºC and 6 Mpa |
| 650-750 Mpa |
15-25% |
HV220-260 |
22-27Mpa |
≥100h |
Main physical properties
| Density |
Resistivity |
Melting Point |
Maximum Continuous Working Temperature |
| 7.1g/cm3 |
1.45x10-6Ω.m |
1500ºC |
1400ºC |
Resistance Temperature Coefficient(Ct)
| 800ºC |
1000ºC |
1400ºC |
| 1.03 |
1.04 |
1.05 |
Average Linear Expansion Coefficient
| 20-800ºC |
20-1000ºC |
20-1400ºC |
| 14 |
15 |
16 |
Fast Life
| |
1300ºC |
1350ºC |
| Average Fast Life (Hours) |
110 |
90 |
| Sagging rate after rupture |
8 |
11 |
Testing according to GB/T13300-91 Standard Method