Hastelloy C-4 Alloy C4 N06455 2.4610 Tube

• Customization: Available
• Application: Aviation, Electronics, Industrial, Medical
• Standard: JIS, GB, DIN, BS, ASTM, AISI
• Model NO.: Hastelloy C4
• Alloy: Alloy
• Type: Nickel Plate
• Powder: Not Powder
• Sample: Free
• Delivery Time: 5-15days
• Name: Hastelloy C4
• Surface: Bright
• Criterion: ASTM Aws
• Diameter: 1-200mm
• OEM: Yes
• Transport Package: Wooden Case
• Specification: 1-200.0mm
• Trademark: HUONA
• Origin: Shanghai, China
• HS Code: 7223000000
• Production Capacity: 2000 Tons/Year

Product Description

Hastelloy C-4 Alloy C4 N06455 2.4610 Tube
Hastelloy C-4

Hastelloy C-4 Chemical compostion:

Alloy	%	Ni	Cr	Mo	Fe	C	Mn	Si	Co	S	P	Ti
C-4	Min.	65	14	14
	Max.		18	17	3.0	0.01	1.0	0.08	2.0	0.010	0.025	0.70

Hastelloy C-4 Physical properties:

Density	8.64 g/cm3
Melting point	1350-1400 ºC

Hastelloy C-4 Alloy minimum mechanical properties in the room temperature:

Alloy	Tensile strength Rm N/mm2	Yield strength RP0.2N/mm2	Elongation A5 %
C-4	783	365	55

HASTELLOY C-4 alloy is a nickel-chromium-molybdenum alloy with outstanding
high-temperature stability as evidenced by high ductility and corrosion resistance even
after aging in the 1200 to 1900°F (649 to 1038°C) range. This alloy resists the formation
of grain-boundary precipitates in the weld heat-affected zone, thus making it suitable
for most chemical process applications in the as-welded condition. C-4 alloy also
has excellent resistance to stress-corrosion cracking and to oxidizing atmospheres up to
1900°F (1038°C).
HASTELLOY C-4 alloy has exceptional resistance to wide variety of chemical process
environments. These include hot contaminated mineral acids, solvents, chlorine
and chlorine contaminated media (organic and inorganic), dry chlorine, formic and
acetic acids, acetic anhydride, and seawater and brine solutions.

HASTELLOY C-4 alloy can be forged, hot-upset, and impact extruded. Although the
alloy tends to work-harden, it can be successfully deep-drawn, spun, press formed or
punched. All of the common methods of welding can be used to weld HASTELLOY C-4
alloy, although the oxy-acetylene and submerged arc processes are not recommended
when the fabricated item is intended for use in corrosion service. Special precautions
should be taken to avoid excessive heat input.