| Customization: | Available |
|---|---|
| Application: | Aviation, Electronics, Industrial, Medical, Chemical |
| Standard: | JIS, GB, DIN, BS, ASTM, AISI |
|
Still deciding? Get samples of US$ 20/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Soft magnetic alloys 1J50 / FeNi 50 / Ni 50
Mainly used in two areas for energy conversion and information processing
In the power industry, mainly in the high magnetic field has a high magnetic induction and low core loss of the alloy. In the electronics industry, mainly at low or medium alloy having a high magnetic permeability and low coercive force. At high frequencies shall be made on a thin strip or alloy higher resistivity. Usually with sheet or strip.
Soft magnetic materials in exchange for use, due to the alternating magnetic eddy currents are induced inside the material, resulting in the loss, the smaller the resistance of the alloy, the greater the thickness, the higher the frequency of the alternating magnetic field, eddy current losses greater, magnetic reduce more. For this, the material must be made thinner sheet (tape), and the surface coated with an insulating layer, or the use of certain methods to the surface to form an oxide insulating layer, such alloys commonly used magnesium oxide electrophoresis coating.
Iron-nickel alloy mostly in the alternating magnetic field use, mainly for yoke iron, relay, Small Power Transformers and Magnetically shielded.
The following are details of our products 1J50:
Chemical composition
| composition | C | P | S | Mn | Si |
| ≤ | |||||
| Content(%) | 0.03 | 0.02 | 0.02 | 0.6~1.1 | 0.3~0.5 |
| composition | Ni | Cr | Mo | Cu | Fe |
| Content(%) | 49.0~51.0 | - | - | 0.2 | Bal |
| Shop sign | Linear expansion coefficient | Resistivity (μΩ·m) |
Density (g/cm³) |
Curie point (ºC) |
Saturation magnetostriction coefficient (10-6) |
| 1j50 | 9.20 | 0.45 | 8.2 | 500 | 25.0 |
| shop sign | Annealing medium | heating temperature | Keep the temperature time/h | Cooling rate |
1j50 |
Dry hydrogen or vacuum, pressure is not greater than 0.1 Pa | Along with the furnace heating up 1100~1150ºC | 3~6 |
In 100 ~ 200 ºC / h speed cooling to 600 ºC, fast to 300 ºC draw a charge |
FAQ
1. How long i can get the feedback after we sent the enquiry?
A: We will reply you within 12 hours in working day.
2. How can I get some samples?
A: We are pleased to offer you sample, the delivery time is about 4-7 days.
3. Are you a factory?
A: Yes. We are. We have specialized in this field over 10 Year.
4. What is the delivery time?
A:15 days normally, detail delivery date should be decided according to production season and order quantity.
){kind=link}