Aws 5.14 Ernicrmo-4 TIG Welding Wire

• Customization: Available
• Application: Electronics, Industrial, Medical
• Standard: JIS, GB, DIN, BS, ASTM, AISI
• Model NO.: Ernicrmo-4
• Alloy: Alloy
• Type: Nickel Wire
• Powder: Not Powder
• Sample: Free
• Welding Power: DC
• Delivery Time: 5-15days of Ernicrmo-3
• Name: Ernicrmo-3
• Surface: Bright
• Criterion: ASTM Aws
• Diameter: 1.6mm
• Transport Package: Spool+Case
• Specification: 0.9-4.0
• Trademark: HUONA
• Origin: Shanghai, China
• HS Code: 7505220000
• Production Capacity: 2000 Tons/Year

Product Description

Aws 5.14 Ernicrmo-4 TIG Welding Wire

Product Description
INTRODUCTION
ERNiCrMo-3 provides excellent resistance to oxidizing and reducing environments. The high molybdenum content provides good stress, pitting and crevice corrosion resistance. It is used for welding of nickel-chromium-molybdenum alloys. And for cladding and welding dissimilar base metals such as Ni-Cr-Mo alloys to stainless and carbon steels.
 
Common Names: Oxford Alloy® 625 FM625 Techalloy 625
Standard: AWS 5.14 Class ERNiCrMo-3 / ASME SFA 5.14 Class ERNiCrMo-3 
         UNS N06625  Werkstoff Nr. 2.4831  ISO SNi6625
 
 
ERNiCrMo-3 CHEMICAL COMPOSITION(%)

C	Si	Mn	S	P	Ni	Nb+Ta
≤0.1	≤0.5	≤0.5	≤0.015	≤0.02	≥58.0	3.5-4.15
Al	Ti	Fe	Cu	Cr	Mo	others
≤0.4	≤0.4	≤5.0	≤0.5	20-23	8.0-10	<0.5

ERNiCrMo-4 CHEMICAL COMPOSITION(%)
 

C	Si	Mn	S	P	V	Ni
≤0.02	≤0.08	≤1.00	≤0.03	≤0.40	8.0-10.0	Rem
Fe	Cu	Co	Cr	Mo	W	other
4.0-7.0	≤0.50	≤2.5	14.5-16.5	15.0-17.0	3.0-4.5	≤0.5

 
WELDING PARAMETERS
 


MECHANICAL PROPERTIES

Tensile Strength	114,500 PSI	790 MPA
Yield Strength	85,000 PSI	590 MPA
Elongation	27%

APPLICATIONS
·ERNiCrMo-3 nickel based welding wire is used for joining and overlaying with INCOFLUX NT100 submerged Arc Flux. 
· This alloy can also be used for dissimilar welding using various nickel-chromium-molybdenum alloys and stainless steel, low alloy, and even carbon steels
·  ERNiCrMo-3 is formulated with low iron (less than 1.0%), and high chromium (over 21.5%) to be an excellent choice for overlaying tubes and tube panels where low dilution of iron and high deposits of chromium are required.